Two-component epoxy resin adhesive LOXEAL 44-28
LOX44-28
€22.87
Tax included
€18.90
tax 21% excl.
APPLICATIONS: Bonding and sealing of composites
COLOUR: Black
RESISTANCE TO HANDLING: 13 minutes at 25ºC
FUNCTIONAL CURING: 1 hour at 25ºC
COMPLETE CURING: 48 hours at 60ºC
VISCOSITY: High 100-150 Pa
100% secure payments
LOXEAL 44-28
Loxeal 44-28 is a tough, semi-flexible, fast-acting two-component thisotropic epoxy resin. High temperature resistant.
Particularly suitable for gluing and sealing composites, it also offers good adhesion to different types of materials: wood, metals, ceramics and various types of plastics.
Its high viscosity allows its use in vertical applications and the filling of large gaps.
It offers a tenacious adhesion, with high resistance to impacts, vibrations and high temperatures.
Physical properties:
• Party: A B
• Composition: epoxy resin amines
• Viscosity (+25ºC Pa s): 100thixo 150thixo
• Colour: white black
• Specific weight (g/ml: 1,1 1,1
• Mix ratio 2:1
• Clearance: 3,0 mm
• Shelf life: 1 year +5- +25ºC in original packaging
Properties of the product already cured at +25ºC:
-
Handling time: 13min**
-
Functional hardening time (+60ºC): 1h
-
Final hardening time (+60ºC): 48h
-
Color after mixing: black
Shear resistance (after 48h at +25ºC ISO 4587):
-
Steel 25 N/mm2
-
FRP Glass/Polyester 9 N/mm2
-
FRP Glass/Epoxy 24 N/mm2
-
FRP Carbon/Epoxy 31 N/mm2
-
CFRP/ Aluminum 25 N/mm2
-
CFRP / Steel 23 N/mm2
Peel strength (AI): 250 N/25mm
Temperature range: -40ºC/+120ºC
**Time detected using 3g mix
________________________________________________________________
*For all the information and instructions for use, you can download the TECHNICAL DATA SHEET and SAFETY DATA SHEET below.
- KIND OF PRODUCT
- Adhesive
You might also like